عنوان انگلیسی Effect of different surface treatments on the shear bond strength of nanofilled composite repairs
چکیده انگلیسی مقاله Background. Repairing aged composite resin is a challenging process. Many surface treatment options have been proposed to this end. This study evaluated the effect of different surface treatments on the shear bond strength (SBS) of nanofilled composite resin repairs. Methods. Seventy-five cylindrical specimens of a Filtek Z350XT composite resin were fabricated and stored in 37°C distilled water for 24 hours. After thermocycling, the specimens were divided into 5 groups according to the following surface treatments: no treatment (group 1); air abrasion with 50-µm aluminum oxide particles (group 2); irradiation with Er:YAG laser beams (group 3); roughening with coarse-grit diamond bur + 35% phosphoric acid (group 4); and etching with 9% hydrofluoric acid for 120 s (group 5). Another group of Filtek Z350XT composite resin samples (4×6 mm) was fabricated for the measurement of cohesive strength (group 6). A silane coupling agent and an adhesive system were applied after each surface treatment. The specimens were restored with the same composite resin and thermocycled again. A shearing force was applied to the interface in a universal testing machine. Data were analyzed using one-way ANOVA and post hoc Tukey tests (P < 0.05). Results. One-way ANOVA indicated significant differences between the groups (P < 0.05). SBS of controls was significantly lower than the other groups; differences between groups 2, 3, 4, 5 and 6 were not significant. Surface treatment with diamond bur + 35% phosphoric acid resulted in the highest bond strength. Conclusion. All the surface treatments used in this study improved the shear bond strength of nanofilled composite resin used.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله غزاله احمدی زنوز | ghazaleh ahmadizenouz
assistant professor, department of operative dentistry, faculty of dentistry, babol university of medical scienses, babol, iran


بهناز اسماعیلی | behnaz esmaeili
assistant professor, department of operative dentistry, faculty of dentistry, babol university of medical scienses, babol, iran


arnica تقوایی | arnica taghvaei
dental student, faculty of dentistry, babol university of medical scienses, babol, iran.


زهرا جمالی | zahra jamali
professor, department of pedeatric dentistry, faculty of dentistry, tabriz university of medical sciences, tabriz, iran

سازمان اصلی تایید شده: دانشگاه علوم پزشکی تبریز (Tabriz university of medical sciences)

طلوع جعفری | toloo jafari
assistant professor, department of operative dentistry, faculty of dentistry, babol university of medical scienses, babol, iran


فرشید امیری دانشور | farshid amiri daneshvar
post-graduate student of prosthodontics,department of prosthodontics, , babol university of medical sciences, babol, iran

سازمان اصلی تایید شده: دانشگاه علوم پزشکی بابل (Babol university of medical sciences)

ثریا خفری | soraya khafri
assistant professor, department of biostatistics and epidemiology, faculty of medicine, babol university of medical sciences, babol, iran

سازمان اصلی تایید شده: دانشگاه علوم پزشکی بابل (Babol university of medical sciences)

نشانی اینترنتی http://dentistry.tbzmed.ac.ir/joddd/index.php/joddd/article/view/1796
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/183/article-183-319642.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات