عنوان انگلیسی Comparative evaluation of the effect of manufacturing process on distortion of rotary ProFile and Twisted File: an in vitro SEM study
چکیده انگلیسی مقاله Background and aims. The manufacturing process of rotary Ni-Ti file can influence its resistance to fracture. The rotary ProFile (Dentsply-Maillefer, Baillagues, Switzerland) is manufactured by grinding mechanism whereas Twisted File (Sybron Endo, USA) is manufactured with a twisting method. The purpose of this study was to comparatively evaluate the effect of manufacturing process on distortion of rotary ProFile and Twisted files using scanning electron microscopy after in vitro use. Materials and methods. Five sets of each type of file were used for this study - rotary ProFile (group A) and Twisted file (group B). Each set was used according to manufacturer’s instructions to prepare 5 mesial canals of extracted mandibular molars. The changes in files were observed under a scanning electron microscope at ×18, ×100, ×250 and ×500 magnifications. Observations were classified as intact with no discernible distortion, intact but with unwinding, and fractured. Group A and B were then compared for deformation and fracture using two-proportion z-test. Results. On SEM observation, used rotary ProFile showed microfractures along the machining grooves whereas Twisted file showed crack propagation that was perpendicular to the machining marks. On statistical analysis, no significant difference was found between ProFile and Twisted file for deformation (P=0.642) and fracture (P=0.475). Conclusion. Within the experimental protocol of this study, it was concluded that both ProFile and Twisted files exhibited visible sign of distortion before fracture. But Twisted file gained edge over ProFile because of its manufacture design and unparalleled resistance to breakage.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله swati شارما | swati sharma


rajendra کومار تواری | rajendra kumar tewari


surendra کومار میشرا | surendra kumar mishra


pankaj kharade | pankaj kharade


نشانی اینترنتی http://dentistry.tbzmed.ac.ir/joddd/index.php/joddd/article/view/1805
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/183/article-183-319652.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات