عنوان انگلیسی Comparison of shear bond strength of resin-modified glass ionomer and composite resin to three pulp capping agents
چکیده انگلیسی مقاله Background and aim: Present study was designed to compare the bonding strength of resin-modified glass ionomer (RMGI) and composite resin to mineral trioxide aggregate (MTA), MTA mixed with Na2HPO4 (NAMTA), and calcium-enriched mixture (CEM). Materials and methods: Thirty specimens of each CEM, NAMTA, and MTA were prepared. Composite and RMGI restorations were then placed on the samples (15 samples in six subgroups). Shear bond strength was assessed using universal testing machine. Data were analyzed with two-way ANOVA and post-hoc Tukey test. To compare the bond strength in subgroups, one-away ANOVA was applied. Significance level was set at P 0.05). Conclusion: Regarding shear bond strength to the tested substrates, composite was shown to be superior to RMGI. The bond of resin composite to MTA was weaker than that to CEM and NAMTA.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله امیر احمد عجمی | amir ahmad ajami


المیرا جعفری navimipour | elmira jafari navimipour
tabriz university of medical sciences, iran

سازمان اصلی تایید شده: دانشگاه علوم پزشکی تبریز (Tabriz university of medical sciences)

سیاوش سوادی اسکویی | siavash savadi oskoee


مهرداد لطفی | mehrdad lotfi


مهدی عابد kahnamoui | mehdi abed kahnamoui


مهدی daneshpooy | mehdi daneshpooy


نشانی اینترنتی http://dentistry.tbzmed.ac.ir/joddd/index.php/joddd/article/view/464
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/183/article-183-319762.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات