عنوان انگلیسی Comparison of chamfer and deep chamfer preparation designs on the fracture resistance of zirconia core restorations
چکیده انگلیسی مقاله Background and aims. One of the major problems of all-ceramic restorations is their probable fracture under occlusal force. The aim of the present in vitro study was to compare the effect of two marginal designs (chamfer and deep chamfer) on the fracture resistance of all-ceramic restorations, CERCON. Materials and methods. This in vitro study was carried out with single-blind experimental technique. One stainless steel die with 50’ chamfer finish line design (0.8 mm deep) was prepared using a milling machine. Ten epoxy resin dies were prepared. The same die was retrieved and 50' chamfer was converted into a deep chamfer design (1 mm). Again ten epoxy resin dies were prepared from the deep chamfer die. Zirconia cores with 0.4 mm thickness and 35 µm cement space were fabricated on the epoxy resin dies (10 chamfer and 10 deep chamfer samples). The zirconia cores were cemented on the epoxy resin dies and underwent a fracture test with a universal testing machine and the samples were investigated from the point of view of the origin of the failure. Results. The mean values of fracture resistance for deep chamfer and chamfer samples were 1426.10±182.60 and 991.75±112.00 N, respectively. Student’s t-test revealed statistically significant differences between the groups. Conclusion. The results indicated a relationship between the marginal design of zirconia cores and their fracture resistance. A deep chamfer margin improved the biomechanical performance of posterior single zirconia crown restorations, which might be attributed to greater thickness and rounded internal angles in deep chamfer margins.
کلیدواژه‌های انگلیسی مقاله CAD/CAM,dental restoration,fracture strength,zirconium oxide
نویسندگان مقاله عزت اله جلالیان | ezatollah jalalian
associate professor of prosthetic dentistry of azaduniversity


رقیه رستمی | roghayeh rostami
dentist


berivan آتشکار | berivan atashkar
dentist
نشانی اینترنتی http://dentistry.tbzmed.ac.ir/joddd/index.php/joddd/article/view/269
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/183/article-183-319835.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات